Semiconductor device and manufacturing method thereof

ABSTRACT

In a method for manufacturing a semiconductor device, a first dielectric layer is formed over a substrate. A first set of recesses is formed in the first dielectric layer. A metal layer is formed in the first set of recesses. A set of metal wirings is formed from the metal layer in the first set of recesses. A second set of recesses is formed in the first dielectric layer. A second dielectric layer is formed over the set of metal wirings and in the second set of recesses. A third set of recesses is formed in the first dielectric layer and the second dielectric layer. A third dielectric layer is formed over the metal wirings and in the third set of recesses.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a Divisional Application of U.S. Ser. No. 15/002,095filed Jan. 20, 2016, now U.S. Pat. No. 9,711,391, the subject matter ofwhich is incorporated herein by reference in entirety.

TECHNICAL FIELD

The disclosure relates to a semiconductor integrated circuit, moreparticularly to a semiconductor device having metal wirings and itsmanufacturing process.

BACKGROUND

As the semiconductor industry introduces new generations of integratedcircuits (ICs) having higher performance and greater functionality,multi-layer metal wiring structures disposed over the underlyingelectronic devices, such as transistors, have been employed. To meetrequirements for a higher speed and more reliability, advanced metalwire forming methods and structures have been developed.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detaileddescription when read with the accompanying figures. It is emphasizedthat, in accordance with the standard practice in the industry, variousfeatures are not drawn to scale and are used for illustration purposesonly. In fact, the dimensions of the various features may be arbitrarilyincreased or reduced for clarity of discussion.

FIGS. 1-9 show exemplary sequential processes for manufacturing a metalwiring structure for a semiconductor device according to an embodimentof the present disclosure.

FIGS. 10-16 show exemplary sequential processes for manufacturing ametal wiring structure for a semiconductor device according to anembodiment of the present disclosure.

DETAILED DESCRIPTION

It is to be understood that the following disclosure provides manydifferent embodiments, or examples, for implementing different featuresof the invention. Specific embodiments or examples of components andarrangements are described below to simplify the present disclosure.These are, of course, merely examples and are not intended to belimiting. For example, dimensions of elements are not limited to thedisclosed range or values, but may depend upon process conditions and/ordesired properties of the device. Moreover, the formation of a firstfeature over or on a second feature in the description that follows mayinclude embodiments in which the first and second features are formed indirect contact, and may also include embodiments in which additionalfeatures may be formed interposing the first and second features, suchthat the first and second features may not be in direct contact. Variousfeatures may be arbitrarily drawn in different scales for simplicity andclarity.

Further, spatially relative terms, such as “beneath,” “below,” “lower,”“above,” “upper” and the like, may be used herein for ease ofdescription to describe one element or feature's relationship to anotherelement(s) or feature(s) as illustrated in the figures. The spatiallyrelative terms are intended to encompass different orientations of thedevice in use or operation in addition to the orientation depicted inthe figures. The apparatus may be otherwise oriented (rotated 90 degreesor at other orientations) and the spatially relative descriptors usedherein may likewise be interpreted accordingly. In addition, the term“made of” may mean either “comprising” or “consisting of.”

FIGS. 1-9 show exemplary sequential processes for manufacturing a metalwiring structure for a semiconductor device according to an embodimentof the present disclosure. In FIGS. 1-9, sequential processes formanufacturing one of metal wiring layers (wiring levels), which areformed above a substrate, are illustrated. Although there are corestructures such as transistors or other elements (e.g., contacts etc.)constituting the semiconductor device (hereinafter referred to as“underlying structures”) between the substrate and the metal wiringlayers, detailed illustrations of such underlying structures are omittedin FIGS. 1-9 for simplicity. Metal wirings are conductive patternslaterally extending in the metal wiring layer and may also be called aninterconnection or an interconnect metal layer.

As shown in FIG. 1, a first interlayer dielectric (ILD) layer 10 isformed over the underlying structures 5 disposed over the substrate 1.In some embodiments, the substrate 1 is a semiconductor substrate.Alternatively, the substrate 1 may comprise another elementarysemiconductor, such as germanium; a compound semiconductor includingGroup IV-IV compound semiconductors such as SiC and SiGe, Group III-Vcompound semiconductors such as GaAs, GaP, GaN, InP, InAs, InSb, GaAsP,AlGaN, AnnAs, AlGaAs, GaInAs, GaInP, and/or GaInAsP; or combinationsthereof. In one embodiment, the substrate 1 is a silicon layer of an SOI(silicon-on insulator) substrate. Amorphous substrates, such asamorphous Si or amorphous SiC, or insulating material, such as siliconoxide may also be used as the substrate 1. The substrate 1 may includevarious regions that have been suitably doped with impurities (e.g.,p-type or n-type conductivity).

An interlayer dielectric layer may also be called an inter-metaldielectric (IMD) layer. The first ILD layer 10 is made of, for example,one or more layers of low-k dielectric material. Low-k dielectricmaterials have a k-value (dielectric constant) lower than about 4.0.Some low-k dielectric materials have a k-value lower than about 3.5 andmay have a k-value lower than about 2.5.

The materials for the first ILD layer 10 may include compoundscomprising Si, O, C and/or H, such as SiCOH and SiOC. Organic material,such as polymers, may be used for the first ILD layer 10. For example,the first ILD layer 10 is made of one or more layers of acarbon-containing material, organo-silicate glass, a porogen-containingmaterial, and/or combinations thereof in certain embodiments. Nitrogenis also included in the first ILD layer 10 in some embodiments. Thefirst ILD layer 10 may be a porous layer. The density of the first ILDlayer 10 is less than about 3 g/cm³ in one embodiment and is less thanabout 2.5 g/cm³ in other embodiments. The first ILD layer 10 may beformed by using, for example, plasma-enhanced chemical vapor deposition(PECVD), low pressure CVD (LPCVD), atomic layer CVD (ALCVD), and/or aspin-on technology. In case of PECVD, the film is deposited at asubstrate temperature in a range of about 25° C. to about 400° C. and ata pressure of less than 100 Torr.

In some embodiments, the first ILD layer 10 includes an inter-layerinsulating film and an inter-wire insulating film, such that the metalwirings will be formed mainly in the inter-layer insulating film. Theinter-layer insulating film may include a SiOC film, and the inter-wireinsulating film may include a TEOS (tetraethylorthosilicate) film.

As shown in FIG. 2, first recesses 15 are formed in the first ILD layer10 by using patterning operations including lithography and etchingoperations. In some embodiments, one or more via holes (contact holes)(not shown) to be connected to one or more elements of the underlyingstructure 5 are formed at the bottom of the first recesses 15.

In some embodiments, an etch-stop layer 12 is used so that the bottom ofthe recesses 15 can be defined. For instance, the etch-stop layer 12 maybe utilized to control an end point of the etching operations utilizedto form the first recesses 15. In such embodiments, the first ILD layer10 includes a lower first ILD layer 10A and an upper first ILD layer10B, with the etch-stop layer 12 being between the lower first ILD layer10A and the upper first ILD layer 10B. The materials for the lower firstILD layer 10A and the upper first ILD layer 10B may be the same or maybe different. The etch-stop layer 12 may include silicon oxide, siliconnitride, silicon carbide, silicon oxynitride, or other suitableetch-stop materials. In some cases, the etch-stop layer 12 may includeone or more layers of etch-stop material. If an etch-stop layer is notused, the depth of the first recesses 15 may be controlled bycontrolling an etching time and/or an etching rate of the recessetching. The etch-stop layer 12 is not shown in later figures forsimplicity.

As shown in FIG. 3, a barrier layer 17 is formed in the first recesses15 and over the first ILD layer 10. In some embodiments, the barrierlayer 17 is disposed only on the sidewalls of the first recesses 15. Thebarrier layer 17 may be formed by using chemical vapor deposition (CVD),physical vapor deposition (PVD), atomic layer deposition (ALD), orelectro-plating such as electrodeless plating. The materials for thebarrier layer 17 may include one or more layers of Ta, TaN, Cu, Ru, Co,Ti, and/or TiN. For example, the barrier layer 17 may include a titaniumlayer and titanium nitride layer, where the titanium layer is in contactwith the first ILD layer 10 and the titanium nitride layer is in contactwith the titanium layer. In some embodiments, the thickness of thebarrier layer 17 is from about 5 Å to about 300 Å.

As shown in FIG. 4, a metal layer 18 is formed over the barrier layer17. The metal layer 18 may be formed by CVD, PVD, ALD, and/orelectro-plating. The metal layer 18 may include one or more layers ofAl, Cu, Co, Ru, or Ag. In some embodiments, the metal layer 18 includesCu or Cu-based materials. In such cases, the metal layer 18 may beformed using an electric copper plating (ECP) operation. With the metallayer formation operation, the first recesses 15 are substantially fullyfilled by the metal layer 18. The barrier layer 17 may be utilized toprevent diffusion of the metal layer 18 into the first ILD layer 10.

As shown in FIG. 5, metal wirings 20 and 21 are formed from the metallayer 18. The metal wirings 20 and 21 may be formed using aplanarization operation to remove portions of the metal layer 18 formedon the upper surface of the first ILD layer 10. The planarizationoperation is performed to obtain a desirable thickness and flatness ofthe metal layer 18. In some embodiments, the depth D of the metalwirings 20 and 21 is from about 10 Å to about 3000 Å. A width w₁ of eachof the metal wirings 20 and 21 may be from about 10 Å to about 3000 Å. Adistance w₂ between neighboring (e.g., adjacent) metal wirings may befrom about 10 Å to about 3000 Å. The distance w₂ may be referred to asthe interconnect spacing (e.g., copper interconnect spacing in the caseof copper interconnects). In some embodiments, the distance w₂ is fromabout 800 Å to about 1200 Å.

In some embodiments, the planarization operation includes a chemicalmechanical polishing (CMP) operation. The CMP operation may involve useof a slurry composition that includes oxidizers, corrosion inhibitors,buffering agents, and complexing agents. In the case of a copper CMPoperation, the CMP operation may utilize slurry compositions based onammonium hydroxide, nitric acid, and peroxide solutions. In someembodiments, the copper CMP operation utilizes copper slurries that areacidic solutions with alumina (Al₂O₃) as an abrasive. The CMP operationmay cause a dishing effect for the metal layer 18. CMP defects may bereduced through oxide buffering, post-CMP cleaning, and pH control.

In the CMP operation, a wafer carrier may be used to hold onto a bottomsurface of the substrate 1 in FIG. 1 such that the metal layer 18 isfacing a polishing pad. The polishing pad may be dispersed with theslurry composition and may be supported by a rotary or linear movingplaten. The CMP operation may involve mechanically polishing (e.g.,removing portions of) the metal layer 18 by rotating the metal layer 18(e.g., via rotating the substrate 1) against the polishing pad to obtaina desirable thickness and flatness of the metal layer 18.

Parameters associated with the CMP operation may include, for example, arotational speed of the polishing pad, a downward force applied to themetal layer 18 by the wafer carrier, composition of the slurry, and aflow rate of the slurry. The rotational speed of the polishing pad maybe between 40 revolutions/minute (rpm) and 130 rpm. The downward forcemay be between 2 pounds per square inch (psi) and 8 psi. In someembodiments, the downward force is between 3.5 psi and 5.5 psi. The flowrate of the slurry may be between 80 mL per minute and 200 mL perminute. The CMP operation may be performed until a desirable thicknessand flatness of the metal layer 18 is achieved.

With reference to FIG. 5, after the CMP operation, a top surface of thefirst ILD layer 10 and the metal wirings 20 and 21 may be wet andcovered with the slurry and reaction products of the CMP operation. Asdried slurry is more difficult to remove than wet slurry (e.g., slurryparticles develop stronger chemical bonds as they dry), a post-CMPcleaning operation is generally performed while the slurry is still wet.

The post-CMP cleaning operation may include applying deionized (DI)water to the top surface of the first ILD layer 10 and the metal wirings20 and 21, such as by submerging at least the top surface of the firstILD layer 10 and the metal wirings 20 and 21 in the DI water. Thetemperature of the DI water may be between 22° C. and about 80° C. Afterapplying the DI water, the post-CMP cleaning operation may includeapplying a cleaning solution to the top surface of the first ILD layer10 and the metal wirings 20 and 21, such as by submerging at least thetop surface of the first ILD layer 10 and the metal wirings 20 and 21 inthe cleaning solution. The cleaning solution may include liquids thatare the same as or similar to those included in the slurry, but withoutthe abrasive components (e.g., alumina). The cleaning solution may be ata temperature of between 22° C. and about 80° C. In some embodiments,the cleaning solution and DI water are dispensed on brushes utilized toscrub the top surface of the first ILD layer 10 and the metal wirings 20and 21 while they are being rotated.

The cleaning solution may include an ammonia peroxide mixture (APM)formed of ammonium hydroxide (NH₄OH), hydrogen peroxide (H₂O₂), and DIwater. In some embodiments, the volume ratios of NH₄OH, H₂O₂, and DIwater, respectively, are between about 0.2:1:5 to 1:1:5. In other cases,the cleaning solution may include diluted hydrofluoric acid (DHF) in DIwater, where the concentration of HF is between about 0.2% and about1.0%.

After the post-CMP cleaning operation, a DI water rinse and a dryingoperation may be performed on the structure of FIG. 5 to remove theslurry and reaction products of the CMP operation from the top surfaceof the first ILD layer 10 and the metal wirings 20 and 21. The dryingoperation may include utilization of a spin dryer in the presence of aflow of nitrogen gas (e.g., hot nitrogen gas), isopropyl alcohol (IPA)vapor dryer, or other drying mechanism. The structure of FIG. 5 is thenready for subsequent operations.

As shown in FIG. 6, second recesses 25 are formed in the first ILD layer10 by performing patterning operations including lithography and etchingoperations. In FIG. 6, one of the second recesses 25 is between theadjacent metal wirings 20 and 21. The lithography and etching operationsmay be performed after the post-CMP cleaning operation. The etchingoperation may include a self-aligned etch-back operation that isperformed to remove a portion of the first ILD layer 10. The etch-backoperation may utilize a dry etching operation, such as a reactive-ionetching (RIE) operation (e.g., deep RIE operation). In some embodiments,the depth d₁ of the second recesses 25 is from about 5 Å to about 500 Å.

The etch-back operation may utilize a fluorine-based plasma chemistry toperform dielectric etching of the first ILD layer 10. In someembodiments, plasmas containing fluorocarbon-based etch gases, such asCF₄ gas, CHF₃ gas, C₂F₆ gas, and C₃F₆ gas, are utilized to etch thefirst ILD layer 10. In some cases, additive gases such as H₂ and O₂ maybe added to the etch gases. In some embodiments, the etch rate isbetween 10 Å per second and 100 Å per second.

As shown in FIG. 7, a first dielectric barrier layer 22 is formed overthe top surface of the first ILD layer 10 and the top surface of themetal wirings 20 and 21 by performing a dielectric barrier depositionoperation (e.g., PECVD operation). A portion of the first dielectricbarrier layer 22 is disposed in the recess between the metal wirings 20and 21. The first dielectric barrier layer 22 is made of, for example,one or more layers of low-k dielectric material. For example, the firstdielectric barrier layer 22 may include one or more layers of SiC, SiCN,SiOC, AlN, AlO_(x), and/or AlON.

In some embodiments, the depth d₂ from the top surface of the firstdielectric barrier layer 22 to the top surface of the etched portion ofthe first ILD layer 10 is from about 5 Å to about 500 Å. A small ditchof depth d₃ may form as a result of the dielectric barrier depositionoperation. The depth d₃ may be from about 5 Å to about 300 Å.

In some embodiments, a treatment operation is performed to remove oxidefrom the top surface of the metal wirings 20 and 21 prior to forming thefirst dielectric barrier layer 22 over the top surface of the first ILDlayer 10 and the top surface of the metal wirings 20 and 21. Thetreatment operation may be referred to as an oxide cleaning operation.The oxide may form on the top surface of the metal wirings 20 and 21when the metal material of the metal wirings 20 and 21 is exposed to andreacts with oxygen (e.g., in air or water). For example, when the metalwirings 20 and 21 include copper, a copper oxide (e.g., Cu or Cu₂O) maybe formed on the surface of the copper due to a reaction between thecopper and oxygen. Presence of the oxide may increase electricalresistance of the metal wirings 20 and 21 if not removed.

The treatment operation may include a plasma treatment operation. Theplasma treatment operation may utilize a treatment gas and a carriergas. The treatment gas may include a hydrogen-containing gas. In someembodiments, the treatment gas includes ammonia (NH₃), silane (SiH₄),methane (CH₄), hydrogen gas (H₂), phosphane (PH₄), or other suitabletreatment gases. The carrier gas may be an inert gas. In someembodiments, the carrier gas includes nitrogen gas (N₂), argon (Ar),helium (He), or other suitable carrier gases. The treatment gas may beexcited to form a reaction gas. The reaction gas may react with theoxide on the metal wirings 20 and 21 and remove the oxide from the metalwirings 20 and 20 (e.g., through a reduction reaction). In someembodiments, a flow rate of the carrier gas ranges from about 10standard cubic centimeters per minute (sccm) to about 30000 sccm. Thetreatment gas may be excited using microwaves. In some embodiments, themicrowaves have a frequency of from about 13 megahertz (MHz) to about 14MHz.

As shown in FIG. 8, third recesses 35 are formed by performingpatterning operations including lithography and etching operations. Theetching operation may include a self-aligned etch-back operation toremove a portion of the first ILD layer 10 and the first dielectricbarrier layer 22. The etch-back operation may utilize a dry etchingoperation, such as an RIE operation (e.g., deep RIE operation). Thedepth d₄ of the third recesses 35 may be measured from a top surface ofthe metal wirings 20 and 21 to the top surface of the etched portion ofthe first ILD layer 10. The depth d₄ may extend through an entirethickness of the second dielectric barrier layer 22. The depth d₄ may befrom about 5 Å to about 300 Å. In some embodiments, the depth d₄ is from30 Å to about 80 Å. In some embodiments, the depth d₁ is from about 80 Åto about 120 Å, the depth d₂ is from about 80 Å to about 140 Å, thedepth d₃ is from about 40 Å to about 60 Å, and the depth d₄ is fromabout 150 Å to about 200 Å.

The etch-back operation for FIG. 8 may be similar to the etch-backoperation described above with respect to FIG. 6. For example, afluorine-based plasma chemistry may be utilized to etch a portion of thefirst ILD layer 10 and the first dielectric barrier layer 22. In somecases, the etch-back operation for FIG. 8 may also include a metal etchoperation. The metal etch operation may be utilized to etch the firstdielectric barrier layer 22 in cases that the first dielectric barrierlayer 22 contains metallic material (e.g., Al, Ti). In some embodiments,plasmas containing chlorine-based etch gases, such as Cl₂ gas, areutilized to etch the first dielectric barrier layer 22. In some cases,additive gases such as H₂ and O₂ may be added to the etch gases. In someembodiments, the etch rate for the etch-back operation (e.g., thedielectric etch and metal etch) is between 10 Å per second and 100 Å persecond.

As shown in FIG. 9, a second dielectric barrier layer 27 is formed overthe top surface of the first ILD layer 10, the top surface of the firstdielectric barrier layer 22, and the top surface of the metal wirings 20and 21 by performing a dielectric barrier deposition operation. Thesecond dielectric barrier layer 27 is made of, for example, one or morelayers of low-k dielectric material. For example, the second dielectricbarrier layer 27 includes one or more layers of SiC, SiCN, SiOC, AlN,AlO_(x), AlON, and/or oxygen doped (silicon) carbide (ODC). In someembodiments, the second dielectric barrier layer 27 includes ODC, whereits precursors include carbon dioxide (CO₂) and nitrogen doped (silicon)carbide (NDC). The first dielectric barrier layer 22 and the seconddielectric barrier layer 27 may be the same or different material(s). Insome embodiments, the thickness of the second dielectric barrier layer27 is from about 10 Å to about 100 Å.

In FIG. 9, a portion 29 of the second dielectric barrier layer 27 isdisposed in the recess between the metal wirings 20 and 21. The portion29 of the second dielectric barrier layer 27 may include a firstsidewall and a second sidewall, with a recess between the first sidewalland second sidewall. One or more of the sidewalls of the seconddielectric barrier layer 27 may be in contact with respective sidewallsformed of respective portions of the ILD layer 10 and respectiveportions of the first dielectric barrier layer 22. In some embodiments,the portion 29 of the second dielectric barrier layer 27 is disposed inthe recess such that the portion 29 includes an upper portion that isabove the first dielectric barrier layer 22 and a lower portion that isbelow the first dielectric barrier layer 22. The lower portion of theportion 29 may be surrounded by the first ILD layer 10. The portion 29may also include a middle portion that is spatially between the upperportion and the lower portion. In some embodiments, the sum of thethicknesses of the middle and lower portions of the portion 29constitutes the depth d₄ labeled in FIG. 8, and the thickness of theupper portion of the portion 29 constitutes the thickness of the seconddielectric barrier layer 27. The barrier layer 17 may be in contact withthe first ILD layer 10, the first dielectric barrier layer 22, and thesecond dielectric barrier layer 27.

The first dielectric barrier layer 22 and the second dielectric barrierlayer 27 may be utilized as a structural ditch to enlarge a diffusionpath for ions of the metal wirings 20 and 21. Under an electric field,the ions of the metal wiring 20 may diffuse from the interface betweenthe metal wiring 20 and the first dielectric barrier layer 22 and theinterface between the metal wiring 20 and the second dielectric barrierlayer 27 to a neighboring metal wiring, such as the metal wiring 21, orvice versa. When the metal wirings 20 and 21 are made of Cu, thediffusion path for Cu ions is enlarged through the utilization of thefirst dielectric barrier layer 22 and the second dielectric barrierlayer 27.

Enlargement of the diffusion path between the metal wirings 20 and 21may allow improvements in the inter-metal dielectric (IMD)time-dependent dielectric breakdown (TDDB) and voltage breakdown V_(bd)margin. The voltage breakdown V_(bd) of the first ILD layer 10 is thevoltage at which a portion of the first ILD layer 10 becomes conductive.With the first dielectric barrier layer 22 and the second dielectricbarrier layer 27, the voltage breakdown V_(bd) of the first ILD layer 10may be in the range from about 4 V to about 9 V. In some embodiments,the voltage breakdown V_(bd) of the first ILD layer 10 is in the rangefrom about 4.5 V to about 5.5 V. In some embodiments, an interconnect(e.g., Cu interconnect) minimum spacing is enlarged by about 20 Å to 30Å. In some embodiments, the TDDB of the first ILD layer 10 is improvedby an order of magnitude. For example, the lifetime of the first ILDlayer 10 without enlarging the diffusion path may be at least 10 years(e.g., per manufacturing specification) whereas the lifetime of thefirst ILD layer 10 with the enlargement of the diffusion path isprojected to be at least 100 years. The plasma treatment may be utilizedto increase adhesion of the metal wirings 20 and 21 and the first ILDlayer 10 to a dielectric material to be disposed over the metal wirings20 and 21 and the first ILD layer 10. The enlargement of the diffusionpath may counteract the scaling down of the interconnect minimum spacingand lower TDDB reliability generally associated with more advanced nodes(e.g., 7 nm node technology).

In some embodiments, the semiconductor device includes a single layer 60of a metal wiring structure, as shown in FIG. 9. Additional layers ofmetal wiring structures may also be utilized in other embodiments. Forexample, FIGS. 10-16 show exemplary sequential processes formanufacturing a second metal wiring structure over the metal wiringstructure formed in FIGS. 1-9, according to an embodiment of the presentdisclosure.

As shown in FIG. 10, a second ILD layer 40 is formed over the metalwiring structure shown in FIG. 9. The second ILD layer 40 is made of,for example, one or more layers of low-k dielectric material. The secondILD layer 40 may use the same or different materials from the first ILDlayer 10. The thickness T of the second ILD layer 40 may be from about100 Å to about 10000 Å.

As shown in FIG. 11, second recesses 43 and 44 are formed in the secondILD layer 40 by using patterning operations including lithography andetching operations. As shown in FIG. 12, a third recess 45 is formed inthe second recess 44 by using patterning operations includinglithography and etching operations. As shown in FIG. 13, a secondbarrier layer 47 is formed in the second recesses 43 and 44 and thethird recess 45 and over the second ILD layer 40. The second barrierlayer 47 may be formed in a similar manner and using the samematerial(s) as described with respect to FIG. 3.

As shown in FIG. 14, a second metal layer 48 is formed over the secondbarrier layer 47. The second metal layer 48 may be formed in a similarmanner and using the same material(s) as described with respect to FIG.4 for the first metal layer 18. As shown in FIG. 15, metal wirings 50and 51 are formed from the metal layer 48. The metal wirings 50 and 51may be formed in a similar manner as described with respect to FIG. 5for the metal wirings 20 and 21. For example, the metal wirings 50 and51 may be formed using a CMP operation, such as that described withrespect to FIG. 5. The CMP operation may be followed by a post-CMPcleaning operation, which in turn is followed by a DI water rinse and adrying operation. The metal wiring 51 includes a lower portion 51A thatfills the third recess 45 and an upper portion 51B that fills the secondrecess 44. The lower portion 51A may be utilized as a through-via forconnecting the upper portion 51B to the metal wiring 21.

As shown in FIG. 16, a third dielectric barrier layer 52 and a fourthdielectric barrier layer 57 are formed. In some embodiments, to arriveat FIG. 16 from FIG. 15, the operations shown in FIGS. 6 through 9 areutilized. The third dielectric barrier layer 52 may be formed in asimilar manner and using the same material(s) as described with respectto the first dielectric barrier layer 22. The fourth dielectric barrierlayer 57 may be formed in a similar manner and using the samematerial(s) as described with respect to the third dielectric barrierlayer 27.

Similar to the first dielectric barrier layer 22 and the seconddielectric barrier layer 27, the third dielectric barrier layer 52 andthe fourth dielectric barrier layer 57 may be utilized as a structuralditch to enlarge a diffusion path for metal wiring ions. For the thirddielectric barrier layer 52 and the fourth dielectric barrier layer 57,the diffusion path for ions may be enlarged between the metal wirings 50and 51. With the third dielectric barrier layer 52 and the fourthdielectric barrier layer 57, the voltage breakdown V_(bd) of the secondILD layer 40 may be in the range from about 4 V to about 9 V. In someembodiments, the voltage breakdown V_(bd) of the second ILD layer 40 isin the range from about 4.5 V to about 5.5 V. In some embodiments, aninterconnect (e.g., Cu interconnect) minimum spacing may be enlarged byabout 20 Å to 30 Å.

With respect to FIG. 16, the metal wiring structure includes the firstlayer 60 from FIG. 9 and a second layer 70. Each of the first layer 60and the second layer 70 may be referred to as a damascene layer. One ormore additional layers of metal wiring structure may be disposed underthe first layer 60 and/or one or more additional layers of metal wiringstructure may be disposed above the second layer 70. Dielectric barrierlayers with structural ditches formed therein may be utilized in theseadditional layers to enlarge respective diffusion paths.

Enlargement of the respective diffusion paths between metal wirings ofeach of the layers of metal wiring structures may allow improvements inthe IMD TDDB and V_(bd) margin in each of the layers. The voltagebreakdown V_(bd) of an ILD layer (e.g., the ILD layer 10) may be in therange from about 4 V to about 9 V, relative to a range of about 3 V toabout 3.5 V in a case without enlarged diffusion paths. In someembodiments, the voltage breakdown V_(bd) of an ILD layer is in therange from about 4.5 V to about 5.5 V. In some embodiments, the TDDB ofthe ILD layer is improved by an order of magnitude. Furthermore, theenlarged diffusion paths may allow an increase in the minimum spacingbetween two neighboring metal wirings for each of the layers of metalwiring structures. In some embodiments, the minimum spacing is enlargedby about 20 Å to 30 Å. The enlargement of the diffusion path maycounteract the scaling down of the interconnect minimum spacing andlower TDDB reliability generally associated with more advanced nodes(e.g., 7 nm node technology).

It will be understood that not all advantages have been necessarilydiscussed herein, no particular advantage is required for allembodiments or examples, and other embodiments or examples may offerdifferent advantages.

In accordance with one aspect of the present disclosure, in a method formanufacturing a semiconductor device, a first dielectric layer is formedover a substrate. A first plurality of recesses is formed in the firstdielectric layer. A metal layer is formed in the first plurality ofrecesses. A plurality of metal wirings is formed in the first pluralityof recesses by performing a planarization operation on the metal layer.A second plurality of recesses is formed in the first dielectric layer.A second dielectric layer is formed over the plurality of metal wiringsand in the second plurality of recesses. A third plurality of recessesis formed in the first dielectric layer and the second dielectric layer.A third dielectric layer is formed over the plurality of metal wiringsand in the third plurality of recesses.

In accordance with another aspect of the present disclosure, asemiconductor device includes a first dielectric layer disposed over asubstrate. A plurality of metal wirings is surrounded by the firstdielectric layer. A second dielectric layer is disposed over a portionof the first dielectric layer, wherein a portion of the seconddielectric layer is disposed in a recess between two adjacent metalwirings of the plurality of metal wirings. A third dielectric layer isdisposed over the first dielectric layer, the second dielectric layer,and the plurality of metal wirings, wherein a portion of the thirddielectric layer is disposed in the recess between the two metalwirings.

In accordance with one aspect of the present disclosure, in a method formanufacturing a semiconductor device, a first dielectric layer is formedover a substrate. A first plurality of recesses is formed in the firstdielectric layer. A plurality of metal wirings is formed in the firstplurality of recesses. A second plurality of recesses is formed, whereinat least one of the second plurality of recesses is formed between twoneighboring metal wirings of the plurality of metal wirings. A seconddielectric layer is formed over the plurality of metal wirings and inthe second plurality of recesses. A third plurality of recesses isformed, wherein at least one of the third plurality of recesses isbetween the two neighboring metal wirings of the plurality of metalwirings. A third dielectric layer is formed over the plurality of metalwirings and in the third plurality of recesses.

The foregoing outlines features of several embodiments or examples sothat those skilled in the art may better understand the aspects of thepresent disclosure. Those skilled in the art should appreciate that theymay readily use the present disclosure as a basis for designing ormodifying other processes and structures for carrying out the samepurposes and/or achieving the same advantages of the embodiments orexamples introduced herein. Those skilled in the art should also realizethat such equivalent constructions do not depart from the spirit andscope of the present disclosure, and that they may make various changes,substitutions, and alterations herein without departing from the spiritand scope of the present disclosure.

What is claimed is:
 1. A semiconductor device, comprising: a firstdielectric layer disposed over a substrate; a plurality of metal wiringssurrounded by the first dielectric layer; a second dielectric layerdisposed over a portion of the first dielectric layer, wherein a portionof the second dielectric layer is disposed in a first recess between twoadjacent metal wirings of the plurality of metal wirings; and a thirddielectric layer disposed over the first dielectric layer, the seconddielectric layer, and the plurality of metal wirings, wherein a portionof the third dielectric layer is disposed in the first recess betweenthe two metal wirings, wherein the portion of the third dielectric layercomprises an upper portion and a lower portion, the upper portion beingabove the second dielectric layer and the lower portion being below thesecond dielectric layer.
 2. The semiconductor device of claim 1, furthercomprising a barrier layer between the plurality of metal wirings andthe first dielectric layer, the barrier layer being in contact with thefirst dielectric layer, the second dielectric layer, and the thirddielectric layer.
 3. The semiconductor device of claim 1, wherein thelower portion is surrounded by the first dielectric layer.
 4. Thesemiconductor device of claim 1, wherein the portion of the thirddielectric layer is in contact with the first dielectric layer and asidewall, the sidewall being formed of a portion of the first dielectriclayer and a portion of the second dielectric layer.
 5. The semiconductordevice of claim 1, wherein the portion of the third dielectric layercomprises a first sidewall and a second sidewall, and a second recess isbetween the first sidewall and the second sidewall.
 6. The semiconductordevice of claim 1, wherein a thickness of the third dielectric layer isin a range of 10 Å to 100 Å.
 7. A semiconductor device, comprising: apair of adjacent metal wirings in a first dielectric layer disposed overa substrate; a second dielectric layer disposed over a portion of thefirst dielectric layer surrounding each of the pair of adjacent metalwirings; and a third dielectric layer disposed over the plurality ofmetal wirings and surrounding each of the two metal wirings, wherein adepth of the third dielectric layer in the first dielectric layer isgreater than a depth of the second dielectric layer in the firstdielectric layer, and wherein the second and third dielectric layers aredifferent materials.
 8. The semiconductor device of claim 7, furthercomprising a barrier layer between the plurality of metal wirings andthe first dielectric layer, the barrier layer being in contact with thefirst dielectric layer, the second dielectric layer, and the thirddielectric layer.
 9. The semiconductor device of claim 7, wherein thethird dielectric layer comprises an upper portion and a lower portion,the upper portion being above the second dielectric layer and the lowerportion being below the second dielectric layer.
 10. The semiconductordevice of claim 9, wherein the lower portion is surrounded by the firstdielectric layer.
 11. The semiconductor device of claim 7, wherein aportion of the third dielectric layer between the pair of adjacent metalwirings comprises a first sidewall and a second sidewall with aconnecting portion between the first sidewall and the second sidewall.12. The semiconductor device of claim 7, wherein a thickness of thethird dielectric layer is in a range of 10 Å to 100 Å.
 13. Asemiconductor device, comprising: a pair of adjacent metal wirings in afirst dielectric layer disposed over a substrate; a second dielectriclayer disposed over a portion of the first dielectric layer surroundingeach of the pair of adjacent metal wirings; a third dielectric layerdisposed over the plurality of metal wirings and surrounding each of thetwo metal wirings; a fourth dielectric layer disposed over the thirddielectric layer and between the two metal wirings; a third metal wiringsurrounded by the fourth dielectric layer, wherein the third metalwiring is in contact with one of the pair of adjacent metal wirings; anda barrier layer between the third metal wiring and the fourth dielectriclayer.
 14. The semiconductor device of claim 13, wherein the fourthdielectric layer comprises an upper portion and a lower portion, theupper portion being above the second dielectric layer and the lowerportion being below the second dielectric layer.
 15. The semiconductordevice of claim 14, wherein the lower portion is surrounded by the thirddielectric layer.
 16. The semiconductor device of claim 13, furthercomprising a fourth metal wiring formed over another of the pair ofadjacent wirings.
 17. The semiconductor device of claim 16, furthercomprising a fifth dielectric layer disposed over the fourth dielectriclayer and surrounding each of the third metal wiring and the fourthmetal wiring.
 18. The semiconductor device of claim 17, furthercomprising a sixth dielectric layer disposed over the fourth dielectriclayer, the fifth dielectric layer, the third metal wiring, and thefourth metal wiring.
 19. The semiconductor device of claim 13, wherein aportion of the third dielectric layer between the pair of adjacent metalwirings comprises a first sidewall and a second sidewall with aconnecting portion between the first sidewall and the second sidewall.20. The semiconductor device of claim 13, further comprising a barrierlayer between the plurality of metal wirings and the first dielectriclayer, the barrier layer being in contact with the first dielectriclayer, the second dielectric layer, and the third dielectric layer.